We are glad to share with you about the results of our work, company news, and give you timely developments and personnel appointment and removal conditions.
Recently, Mr. Weng found that the brightness of the workpiece coating was poor during the process of using the tin plating additive, and there was color fad...
Plating plant in the production process, should have encountered this situation: that is, the entire acid copper workpiece brightness is not good, even if i...
When using alkaline zinc plating additives, sometimes the following phenomenon occurs: the barrel suddenly explodes while rotating. What is the reason for t...
In the chrome plating process, sometimes the surface of the workpiece produced is cracked at the tip position or edge area, which can seriously affect the a...
Mr. Xiao from Suzhou, Jiangsu is the owner of a zinc plating factory, mainly engaged in the processing and production of various hardware zinc plating.
In the past month, the coating of terminal pieces produced by Mr. Duan has always been foggy after bright tin plating, and the inspection and treatment of t...
Recently, a batch of steel ball valve workpieces produced by Mr. Feng have been coated with 10~15 μ m thick electroless nickel coating, which is very brittl...
In our daily nickel-chromium plating process, sometimes the coating of the workpiece is flowered after chrome-plating, which will affect the appearance qual...
Mr. Yang's screws had no problem with the coating after zinc acid plating, but when plating a batch of spring parts, the coating of the workpiece always pee...
When Mr. Dong's hinge workpiece is produced with barrel nickel brightener, although there is a slight blackening phenomenon in the low current area of the c...